S9.9 - Z - Additives
S 9.9 Z - Additives
S 9.9.1 Standox(R) 2K Plasticizer (new)
S 9.9.1.1 Processing
S 9.9.2 Standox(R) 2K Matting Agent MIX 606
S 9.9.2.1 Processing with Standocryl(R) 2K Topcoat
S 9.9.2.2 Processing with Standocryl(R) 2K HS Topcoat
S 9.9.2.3 Standocryl(R) 2K Topcoat matting table
S 9.9.2.4 Standocryl(R) 2K HS Topcoat matting table
S 9.9.1 Standox(R) 2K Plasticizer (new)
WARNING: -> 2 "Safety regulations" and read the product-specific safety instructions on the container labels.
Description:
Elastic-rendering additive for:
- Standocryl(R) 2K Topcoat
- Standocryl(R) 2K HS Topcoat
- Standocryl(R) 2K HS Clear
- Standocryl(R) 2K Crystal Clear
- Standocryl(R) 2K MS Express Clear
- Standocryl(R) 2K System Clear
- Standox(R) 2K Nonstop Primer Filler
- Standox(R) 2K Universal Filler
Properties:
- Gives 2K products the necessary permanent elasticity for plastic paint finishes.
Base surfaces:
- Please refer to the respective data sheets
NOTE:
- Raw material base: Special polymers
- Flash point: 27° C/80.6° F
- Spec. weight: 1.05 g/cm3
- Solid content: 77.0% weight/72.6% vol.
- Clean equipment after use with cleaning thinner
VOC value:
- 233 g/l
WARNING: 2K paints react with moisture. All work equipment, mixing vessels, etc. must therefore be completely water-free.
S 9.9.1.1 Processing
S 9.9.2 Standox(R) 2K Matting Agent MIX 606
WARNING: -> 2 "Safety regulations" and read the product-specific safety instructions on the container labels.
Description:
- 2K matting agent for Standocryl(R) 2K Topcoat and Standocryl(R) 2K HS Topcoat
Properties:
- Allows you to vary the gloss level, depending on the quantity added
Higher gloss level:
- Slower thinner
- Higher processing viscosity
- Higher dry coat thickness
- Shorter drying times
- Faster drying
Lower gloss level:
- Faster thinner
- Lower processing viscosity
- Lower dry coat thickness
- Longer drying times
- Air drying
Base surfaces:
- See material data sheets -> S 9.7.2 "Standocryl(R) 2K Topcoat" and -> S 9.7.4 "Standocryl(R) 2K HS Topcoat"
NOTE:
- Raw material base: Special polymers
- Flash point: 23° C/73.4° F
- Spec. weight: 1.13 g/cm3
- Solid content: 47.6% weight/32.8% vol.
- It is not possible to matt Standocryl(R) 2K HS Clear / Standocryl(R) 2K Crystal Clear / Standocryl(R) 2K MS Express Clear / Standocryl(R) 2K System Clear
- The matting agent is added in accordance with the Standox matting table
- Stir the topcoat and matting agent mixture before adding hardener
- Standox(R) 2K Matting Agent MIX 606 must always be hardened
- Clean equipment after use with cleaning thinner
VOC value:
- 590 g/l
WARNING: 2K paints react with moisture. All work equipment, mixing vessels, etc. must therefore be completely water-free.
S 9.9.2.1 Processing with Standocryl(R) 2K Topcoat
S 9.9.2.2 Processing with Standocryl(R) 2K HS Topcoat
S 9.9.2.3 Standocryl(R) 2K Topcoat matting table
S 9.9.2.4 Standocryl(R) 2K HS Topcoat matting table